Granite 280 Semi-Gloss BioThane is popular for its superior adhesion properties (nearly 300% higher than any other coated webbing) and its "dressed leather" finish.
Profile | Thickness | Break Strength (* See footnote below) | Buckle Pull Strength (** See footnote below) | Available Widths | Adhesion |
---|---|---|---|---|---|
![]() B10 Super Flex |
.055" - .065" 1.40mm - 1.65mm |
1000lbs (453.592kg) | 200lbs (90.719kg) | 3/8", 1/2", 9/16", 5/8", 3/4", 7/8", 1", 1 1/8", 1 1/4", 1 1/2", 2", 2 1/2", 3", 4" | 20 |
![]() B10 High Flex |
.075" - .085" 1.91mm - 2.16mm |
1000lbs (453.592kg) | 200lbs (90.719kg) | 3/8", 1/2", 9/16", 5/8", 3/4", 7/8", 1", 1 1/8", 1 1/4", 1 1/2", 2", 2 1/2", 3", 4" | 20 |
![]() B10 Standard |
.095" - .105" 2.41mm - 2.67mm |
1000lbs (453.592kg) | 200lbs (90.719kg) | 3/8", 1/2", 9/16", 5/8", 3/4", 7/8", 1", 1 1/8", 1 1/4", 1 1/2", 2", 2 1/2", 3", 4" | 20 |
![]() B10 Grooved |
.095" - .105" 2.41mm - 2.67mm |
1000lbs (453.592kg) | 200lbs (90.719kg) | 3/8", 1/2", 9/16", 5/8", 3/4", 7/8", 1", 1 1/8", 1 1/4", 1 1/2", 2", 2 1/2", 3", 4" | 20 |
![]() B10 Beaded |
.150" - .170" 3.81mm - 4.32mm |
1000lbs (453.592kg) | 200lbs (90.719kg) | 3/8", 1/2", 9/16", 5/8", 3/4", 7/8", 1", 1 1/8", 1 1/4", 1 1/2", 2", 2 1/2", 3", 4" | 20 |
![]() B10 Ex Thick Grooved |
.125" - .135" 3.17mm - 3.43mm |
1000lbs (453.592kg) | 200lbs (90.719kg) | 3/8", 1/2", 9/16", 5/8", 3/4", 7/8", 1", 1 1/8", 1 1/4", 1 1/2", 2", 2 1/2", 3", 4" | 20 |
![]() B30 Super Heavy Grooved |
.130" - .160" 3.30mm - 4.06mm |
3000lbs (1360.777kg) | 700lbs (317.515kg) | 3/4", 1", 1 1/4", 1 1/2", 2" | 17 |
![]() B30 Super Thick |
.175" - .195" 4.45mm - 4.95mm |
3000lbs (1360.777kg) | 700lbs (317.515kg) | 3/4", 1", 1 1/4", 1 1/2", 2" | 17 |
![]() B30 Super Thick Grooved |
.175" - .195" 4.45mm - 4.95mm |
3000lbs (1360.777kg) | 700lbs (317.515kg) | 3/4", 1", 1 1/4", 1 1/2", 2" | 17 |
* Break strength value is per inch of width. Example 2″ (50.8mm) is 2000lbs (907.1847kg) or 3/4″ (19.05mm) is 750lbs (340.194kg). ** All Buckle Pull Strength values are based on a 1″ wide specimen. |
Flexibility of Coated B10 Web (pounds force to bend 4″ sample 90°) | 2.89 |
---|---|
Polymer | TPU |
Webbing | PET |
Appearance | Semi-Gloss |
Abrasion Resistance (Scale of 1-10, where 1 is poor and 10 is excellent) | 7 |
UV Resistance (Scale of 1-10, where 1 is poor and 10 is excellent) | 7 |
Infrared Reflectance (Black) | Pass |
Modulus of Rigidity @ -35°C (PSI) | 9480 |
Lash-Berg Stiffness @ 45k PSI (°C) | -51.3 |
Tear Resistance Graves (lbs/inch) | 411 |
Coefficient of Friction - Static | 1.65 |
Coefficient of Friction - Kinetic | 1.43 |
Low Temperature Brittleness (°C ǀ °F) | -56 | -68 |
Glass Transition Temperature (°C) | -47.5 |
Vicat Softening (°C) | 65.7 |
Tensile (PSI) | 2940 |
Modulus @ 100% (PSI) | 717 |
Modulus @ 300% (PSI) | 1090 |
Elongation (%) | 680 |
Acetic Acid 20% (% weight change ǀ % volume change) | 9.6 | 10.2 |
Unleaded Gas (% weight change ǀ % volume change) | 33.3 | 47.5 |
ASTM Oil #1 (% weight change ǀ % volume change) | (-)0.1 | (-)0.2 |
Sodium Hydroxide (% weight change ǀ % volume change) | 0.7 | 0.6 |
Sea Water (% weight change ǀ % volume change) | 0.9 | 0.9 |
Bleach (% weight change ǀ % volume change) | 0.8 | 0.8 |
*All colors shown are digital representations and may vary from actual coating color.